Various compounds

General application
Hardness [°ShA]
45-55
Rubber base
SBR
Strength at break [MPa]
5
Abrasion [max cm³]
-
Elongation at break [%]
400

General application
Hardness [°ShA]
72-78
Rubber base
SBR
Strength at break [MPa]
5
Abrasion [max cm³]
-
Elongation at break [%]
200

General application
Hardness [°ShA]
55-65
Rubber base
SBR
Strength at break [MPa]
5
Abrasion [max cm³]
-
Elongation at break [%]
300

General application
Hardness [°ShA]
75-85
Rubber base
SBR
Strength at break [MPa]
5
Abrasion [max cm³]
-
Elongation at break [%]
150

Inner tubes, mould products
Hardness [°ShA]
50-60
Rubber base
IIR
Strength at break [MPa]
11
Abrasion [max cm³]
-
Elongation at break [%]
600

Highly resilient and resistant articles
Hardness [°ShA]
57-63
Rubber base
NR
Strength at break [MPa]
22
Abrasion [max cm³]
-
Elongation at break [%]
450

Gaskets bearings
Hardness [°ShA]
45-55
Rubber base
NR
Strength at break [MPa]
15,5
Abrasion [max cm³]
-
Elongation at break [%]
450

Mould products
Hardness [°ShA]
50-60
Rubber base
CR
Strength at break [MPa]
8
Elongation at break [%]
300